Chapter XIV

Of Perfection--In Little Things--Cleanliness--Alertness--But not
Hurry--Realising your Conditions--False Lead-Lines--Shutting out
Light--Bars--Their Number--Their Importance--Precedence--Observing
your Limitations--A Result of Complete Training--The Special
Limitations of Stained-Glass--Disguising the Lead-Line--No full
Realism--No violent Action--Self-Effacement--No
Craft-Jugglery--Architectural Fitness founded on Architectural
Knowledge--Seeing Work _in Situ_--Sketching in Glass--The Artistic
Use of the Lead--Stepping Back--Accepting Bars and Leads--Loving
Care--White Spaces to be Interesting--Bringing out the "Quality" of
the Glass--Spotting and Dappling--"Builders-Glazing" _versus_
Modern Restoring.

The second question of principle that I would dwell upon is that of _perfection_.

Every operation in the arts should be perfect. It has to be so in most arts, from violin-playing to circus-riding, before the artist dare make his bow to the public.

Placing on one side the question of the higher grades of art which depend upon special talent or genius--the great qualities of imagination, composition, form and colour, which belong to mastership--I would now, in this book, intended for students, dwell upon those minor things, the doing of which well or ill depends only upon good-will, patience, and industry.

Anyone can wash a brush clean; any one can keep the colour on his palette neat; can grind it all up each time it is used; can cover it over with a basin or saucer when his work is over; and yet these things are often neglected, though so easy to do. The painter will _neglect_ to wash out his brush; and it will be clogged with pigment and gum, get dry, and stick to the palette, and the points of the hair will tear and break when it is removed again by the same careless hand that left it there.

Another will leave portions of his colour, caked and dry, at the edges of his palette for weeks, till all is stale; and then, when the spirit moves him, will some day work this in, full of dirt and dust, with the fresher colour. Everything, everything should be done well! From the highest forms of painting to tying up a parcel or washing out a brush;--all tools should be clean at all times, the handles as well as the hair--there is _no excuse_ for the reverse; and if your tools are dirty, it is by the same defect of your character that will make you slovenly in your work. Painting does not demand the same actual _swiftness_ as some other arts; nevertheless each touch that you place upon the glass, though it may be deliberate, should be deft, athletic, perfect in itself; the nerves braced, the attention keen, and the powers of soul and body as much on the alert as they would need to be in violin-playing, fencing, or dissecting.

This is not to advocate _hurry_. That is another matter altogether, for which also there is no excuse. Never hurry, or ask an assistant to hurry. Windows are delayed, even promises broken (though that can scarce be defended), there may be "ire in celestial minds"; but that is all forgotten when we are dead; and we soon shall be, but not the window.

Another thing to note, which applies generally throughout all practice, is the wisdom, of getting as near as you can to your conditions. For instance, the bits of glass in a window are separated by lead lines; pitch-black, therefore, against the light of day outside. Now, when waxed up on the plate in the shop for painting, these will be separated by thin cracks of light, and in this condition they are usually painted. Can't you do better than that? Don't you think it's worth while spending half-an-hour to paint false lead lines on the back of the plate? A ha'p'orth of lamp-black from the oil-shop, with a little water and treacle and a long-haired brush, like a coach-painter's, will do it for you (see Plate XIII.).

Another thing: when the window is in its place, each _light_ will be surrounded with stone or brick, which, although not so black as the lead lines, will tell as a strong dark against the glass. See therefore that while you are painting, your glass is surrounded by dark, or at any rate not by clear, glittering light. Strips of brown paper, pinned down the sides of the light you are painting, will get the thing quite near to its future conditions.

As you have been told, the work is fixed in its place by bars of iron, and these ought by no means to be despised or ignored or disguised, as if they were a troublesome necessity: you must accept fully and willingly the conditions of your craft; you must pride yourself upon so accepting them, knowing that they are the wholesome checks upon your liberty and the proper boundaries of the field in which you have your appointed work. There should, in any light more than a foot wide, be bars at every foot throughout the length of the light; and these bars should be 1/2 inch, 3/4 inch, or 1 inch in section, according to the weight of the work. The question then arises: Should the bars be set out in their places on the paper, before you begin to draw the cartoon, or should you be perfectly free and unfettered in the drawing and then _make_ the bars fit in afterwards, by moving them up and down as may be needed to avoid cutting across the faces, hands, &c.

I find more difficulty in answering this than any other _technical_ question in this book. I do not think it can be answered with a hard and fast "Yes" or "No." It depends on the circumstances of the case. But I incline towards the side of making it the rule to put the bars in first, and adapt the composition to them. You may think this a surprising view for an artist to take. "Surely," you will say, "that is putting the cart before the horse, and making the more important thing give way to the less!" But my feeling is that reasonable limitations of any kind ought never to be considered as hindrances in a work of art. They are part of the problem, and it is only a spirit of dangerous license which will consider them as bonds, or will find them irksome, or wish to break them through. Stained-glass is not an independent art. It is an accessory to architecture, and any limitations imposed by structure and architectural propriety or necessity are most gravely to be considered and not lightly laid on one side. And in this connection it must be remembered that the bars cannot be made to go _anywhere_ to fit a freely designed composition: they must be approximately at certain distances on account of use; and they must be arranged with regard to each other in the whole of the window on account of appearance.

You might indeed find that, in any single light, it is quite easy to arrange them at proper and serviceable distances, without cutting across the heads or hands of the figures; but it is ten chances to one that you can get them to do so, and still be level with each other, throughout a number of lights side by side.

The best plan, I think, is to set them out on the side of the cartoon-paper before you begin, but not so as to notice them; then first roughly strike out the position your most important groups or figures are to occupy, and, before you go on with the serious work of drawing, see if the bars cut awkwardly, and, if they do, whether a slight shifting of them will clear all the important parts; it often will, and then all is well; but I do not shrink from slightly altering even the position of a head or hand, rather than give a laboured look to what ought to be simple and straightforward by "coaxing" the bars up and down all over the window to fit in with the numerous heads and hands.

If, by the way, I see fit in any case to adopt the other plan, and make my composition first, placing the bars afterwards to suit it, I never allow myself to shift them from the level that is convenient and reasonable for anything _except_ a head; I prefer even that they should cut across a hand, for instance, rather than that they should be placed at inconvenient intervals to avoid it.

The principle of observing your limitations is, I do not hesitate to say, the most important, and far the most important, of all principles guiding the worker in the right practising of any craft.

The next in importance to it is the right exercise of all legitimate freedom _within_ those limitations. I place them in this order, because it is better to stop short, by nine-tenths, of right liberty, than to take one-tenth of wrong license. But by rights the two things should go together, and, with the requisite skill and training to use them, constitute indeed the whole of the practice of a craft.

Modern division of labour is much against both of these things, the observance of which charms us so in the ancient Gothic Art of the Middle Ages.

For, since those days, the craft has never been taught as a whole. Reader! this book cannot teach it you--no book, can; but it can make you--and it was written with the sole object of making you--_wish_ to be taught it, and determine to be taught it, if you intend to practise stained-glass work at all.

Modern stained-glass work is done by numerous hands, each trained in a special skill--to design, or to paint, or to cut, or to glaze, or to fire, or to cement--but none are taught to do all; very few are taught to do more than one or two. How, then, can any either use rightful liberty or observe rightful limitations? They do not know their craft, upon which these things depend. And observe how completely also these two things depend upon each other. You may be rightly free, _because_ you have rightly learnt obedience; you know your limitations, and, _therefore_, you may be trusted to think, and feel, and act for yourself.

This is what makes old glass, and indeed all old art, so full of life, so full of interest, so full of enjoyment--in places, and right places, so full even of "fun." Do you think the charming grotesques that fill up every nook and corner sometimes in the minor detail of mediaeval glass or carving could ever be done by the method of a "superior person" making a drawing of them, and an inferior person laboriously translating them in _facsimile_ into the material? They are what they are because they were the spontaneous and allowed license and play of a craftsman who knew his craft, and could be trusted to use it wisely, at any rate in all minor matters.

THE LIMITATIONS OF STAINED-GLASS.

The limitations of stained-glass can only be learnt at the bench, and by years of patient practice and docile service; but it may be well to mention some of them.

_You must not disguise your lead line._ You must accept it willingly, as a limitation of your craft, and make it contribute to the beauty of the whole.

"But I have a light to do of the 'Good Shepherd,' and I want a landscape and sky, and how ugly lead lines look in a pale-blue sky! I get them like shapes of cloud, and still it cuts the sky up till it looks like 'random-rubble' masonry." Therefore large spaces of pale sky are "taboo," they will not do for glass, and you must modify your whole outlook, your whole composition, to suit what _will_ do. If you must have sky, it must be like a Titian sky--deep blue, with well-defined masses of cloud--and you must throw to the winds resolutely all idea of attempting to imitate the softness of an English sky; and even then it must not be in a large mass: you can always break it up with branched-work of trees, or with buildings.

_There should be no full realism of any kind._

_No violent action must assert itself in a window._

I do not say that there must not, in any circumstances, be any violent action--the subject may demand it; but, if so, it must be so disguised by the craftsmanship of the work, or treated so decoratively, or so mixed up with the background or surroundings, that you do not see a figure in violent action starting prominently out from the window as you stand in the church. But, after all, this is a thing of artistic sense and discretion, and no rules can be formulated. The Parthenon frieze is of figures in rapid movement. Yet what repose! And in stained-glass you must aim at repose. Remember,--it is an accessory to architecture; and who is there that does not want repose in architecture? Name me a great building which does not possess it? How the architects must turn in their graves, or, if living, shake in their shoes, when they see the stained-glass man turned into their buildings, to display himself and spread himself abroad and blow his trumpet!

Efface yourself, my friend; sink yourself; illustrate the building; consider its lines and lights and shades; enrich it, complete it, make people happier to be in it.

_There must be no craft-jugglery in stained-glass._

The art must set the craft simple problems; it must not set tasks that can only be accomplished by trickery or by great effort, disproportioned to the importance of the result. But, indeed, you will naturally get the habit of working according to this rule, and other reasonable rules, if you yourself work at the bench--all lies in that.

_There must be nothing out of harmony with the architecture._

And, therefore, you must know something of architecture, not in order to imitate the work of the past and try to get your own mistaken for it, but to learn the love and reverence and joy of heart of the old builders, so that your spirit may harmonise with theirs.

_Do not shrink from the trouble and expense of seeing the work_ in situ, _and then, if necessary, removing it for correction and amendment._

If you have a large window, or a series of windows, to do, it is often not a very great matter to take a portion of one light at least down and try it in its place. I have done it very often, and I can assure you it is well worth while.

OF MAKING A SKETCH IN GLASS.

But there is another thing that may help you in this matter, and that is to sketch out the colour of your window in small pieces of glass--in fact, to make a scale-sketch of it in glass. A scale of one inch to a foot will do generally, but all difficult or doubtful combinations of colour should be sketched larger--full size even--before you venture to cut.

_Work should be kept flat by leading._

One of the main _artistic_ uses of the leadwork in a window is that, if properly used, it keeps the work flat and in one plane, and allows far more freedom in the conduct of your picture, permitting you to use a degree of realism and fulness of treatment greater than you could do without it. Work may be done, where this limitation is properly accepted and used, which would look vulgar without it; and on the other hand, the most Byzantine rigidity may be made to look vulgar if the lead line is misused. I have seen glass of this kind where the work was all on one plane, and where the artist had so far grasped proper principles as to use thick leads, but had _curved these leads in and out across the folds of the drapery as if they followed its ridges and hollows_--the thing becoming, with all its good-will to accept limitations, almost more vulgar than the discredited "Munich-glass" of a few years ago, which hated and disguised the lead lines.

_You must step back to look at your work as often and as far as you can._

_Respect your bars and lead lines, and let them be strong and many._

_Every bit of glass in a window should look "cared for."_

If there is a lot of blank space that you "don't know how to fill," be sure your design has been too narrowly and frugally conceived. I do not mean to say that there may not be spaces, and even large spaces, of plain quarry-glazing, upon which your subject with its surrounding ornament may be planted down, as a rich thing upon a plain thing. I am thinking rather of a case where you meet with some sudden lapse or gap in the subject itself or in its ornamental surroundings. This is apt specially to occur where it is one which leads rather to pictorial treatment, and where, unless you have "canopy" or "tabernacle" work, as it is called, surrounding and framing everything, you find yourself at a loss how to fill the space above or below.

Very little can be said by way of general rule about this; each case must be decided on its merits, and we cannot speak without knowing them. But two things may be said: First, that it is well to be perfectly bold (as long as you are perfectly sincere), and not be afraid, merely because they are unusual, of things that you really would like to do if the window were for yourself. There are no hard and fast rules as to what may or may not be done, and if you are a craftsman and designer also--as the whole purpose of this book is to tell you you must be--many methods will suggest themselves of making your glass look interesting. The golden rule is to handle every bit of it yourself, and then you will _be_ interested in the ingenuity of its arrangement; the cutting of it into little and big bits; the lacework of the leads; thickening and thinning these also to get bold contrasts of strong and slender, of plain and intricate; catching your pearly glass like fish, in a net of larger or smaller mesh; for, bear in mind always that this question relates almost entirely to the _whiter_ glasses. Colour has its own reason for being there, and carries its own interest; but the most valuable piece of advice that I can think of in regard to stained-glass _treatment_ (apart from the question of subject and meaning) is to _make your white spaces interesting_.

The old painters felt this when they diapered their quarry-glazing and did such grisaille work as the "Five Sisters" window at York. Every bit of this last must have been put together and painted by a real craftsman delighting in his work. The drawing is free and beautiful; the whole work is like jewellery, the colour scheme delightfully varied and irregular. The work was loved: each bit of glass was treated on its merits as it passed through hand. Working in this way all things are lawful; you may even put a thin film of "matt" over any piece to lower it in tone and give it richness, or to bring out with emphasis some quality of its texture. Some bits will have lovely streaks and swirling lines and bands in them--"reamy," as glass-cutters call it--or groups of bubbles and spots, making the glass like agate or pebble; and a gentle hand will rub a little matt or film over these, and then finger it partly away to bring out its quality, just as a jeweller foils a stone. This is quite a different thing from smearing a window all over with dirt to make it a sham-antique; and where it is desirable to lower the tone of any white for the sake of the window, and where no special beauties of texture exist, it is better, I think, to matt it and then take out simple _patterns_ from the matt: not _outlined_ at all, but spotted and streaked in the matt itself, chequered and petalled and thumb-marked, just as nature spots and stripes and dapples, scatters daisies on the grass and snowflakes in the air, and powders over with chessboard chequers and lacings and "oes and eyes of light," the wings of butterflies and birds.

So man has always loved to work when he has been let to choose, and when nature has had her way. Such is the delightful art of the basket and grass-cloth weaver of the Southern seas; of the ancient Cyprian potter, the Scandinavian and the Celt. It never dies; and in some quiet, merciful time of academical neglect it crops up again. Such is the, often delightful, "builders-glazing" of the "carpenters-Gothic" period, or earlier, when the south transept window at Canterbury, and the east and west windows at Cirencester, and many such like, were rearranged with old materials and new by rule of thumb and just as the glazier "thought he would." Heaven send us nothing worse done through too much learning! I daresay he shouldn't have done it; but as it came to him to do, as, probably, he was ordered to do it, we may be glad he did it just so. In the Canterbury window, for instance, no doubt much of the old glass never belonged to that particular window; it may have been, sinfully, brought there from windows where it did belong. At Cirencester there are numbers of bits of canopy and so forth, delightful fifteenth-century work, exquisitely beautiful, put in as best they could be; no doubt from some mutilated window where the figures had been destroyed--for, if my memory serves me, most of them have no figures beneath--and surrounded by little chequered work, and stripes and banding of the glaziers' own fancy. A modern restorer would have delighted to supply sham-antique saints for them, imitating fifteenth-century work (and deceiving nobody), and to complete the mutilated canopies by careful matching, making the window entirely correct and uninteresting and lifeless and accomplished and forbidding. The very blue-bottles would be afraid to buzz against it; whereas here, in the old church, with the flavour of sincerity and simplicity around them, at one with the old carving and the spirit of the old time, they glitter with fresh feeling, and hang there, new and old together, breaking sunlight; irresponsible, absurd, and delightful.