Chapter M: D’Arcet states the analysis of Marseilles soap at (11)

Into the wash-pot, No. 2., filled with melted _grain_ tin, the workman puts the above plates, where the heat detaches the ribs, and drops. There is a longitudinal partition in it, for keeping the drop of tin that rises in washing from entering the vessel where the last dip is given. Indeed, the metal in the wash-pot, after having acted on 60 or 70 boxes, becomes so foul, that the weight of a block (300 cwt.) of it, is transferred into the tin-pot, No. 1., and replaced by a fresh block of grain tin. The plates being lifted out of the wash-pot, with tongs held in the left hand of the workman, are scrubbed on each side with a peculiar hempen brush, held in his right hand, then dipped for a moment in the hot tin, and forthwith immersed in the adjoining grease-pot, No. 3. This requires manual dexterity; and though only three-pence be paid for brushing and tin-washing 225 plates, yet a good workman can earn six shillings and three-pence in twelve hours, by putting 5625 plates through his hands. The final tin-dip is useful to remove the marks of the brush, and to make the surface uniformly bright. To regulate the temperature of the tallow-pot, and time during which the plates are left in it, requires great skill and circumspection on the part of the workman. If kept in it too long, they would be deprived to a certain extent of their silvery lustre; and if too short, streaks of tin would disfigure their surface. As a thick plate retains more heat after being lifted out of the washing-pot, it requires a proportionally cooler grease-pot. This pot has pins fixed within it, to keep the plates asunder; and whenever the workman has transferred five plates to it, a boy lifts the first out into the cold adjoining pan, No. 4.; as soon as the workman transfers a sixth plate, the boy removes the second; and so on. The manufacture is completed by removing the wire of tin left on the under edge of the plates, in consequence of their vertical position in the preceding operations. This is the business of the _list-boy_, who seizes the plates when they are cool enough to handle, and puts the lower edge of each, one by one, into the list-pot, No. 5., which contains a very little melted tin, not exceeding a quarter of an inch in depth. When he observes the wire-edge to be melted, he takes out the plate, and, striking it smartly with a thin stick, detaches the superfluous metal, which leaves merely a faint stripe where it lay. This mark may be perceived on every tin-plate in the market.

The plates are finally prepared for packing up in their boxes, by being well cleansed from the tallow, by friction with bran.

Mr. Thomas Morgan obtained a patent, in September, 1829, for clearing the sheet-iron plates with dilute sulphuric acid in a _hole_, instead of _scaling_ them in the usual way, previous to their being cold rolled, annealed, and tinned; whereby, he says, a better article is produced at a cheaper rate.

_Crystallized tin-plate_, see MOIRÉE METALLIQUE. It would seem that the acid merely lays bare the crystalline structure really present on every sheet, but masked by a film of redundant tin. Though this showy article has become of late years vulgarized by its cheapness, it is still interesting in the eyes of the practical chemist. The English tin-plates marked F, answer well for producing the _Moirée_, by the following process. Place the tin-plate, slightly heated, over a tub of water, and rub its surface with a sponge dipped in a liquor composed of four parts of aquafortis, and two of distilled water, holding one part of common salt or sal ammoniac in solution. Whenever the crystalline spangles seem to be thoroughly brought out, the plate must be immersed in water, washed either with a feather or a little cotton (taking care not to rub off the film of tin that forms the feathering), forthwith dried with a low heat, and coated with a lacquer varnish, otherwise it loses its lustre in the air. If the whole surface is not plunged at once in cold water, but if it be partially cooled by sprinkling water on it, the crystallization will be finely variegated with large and small figures. Similar results will be obtained by blowing cold air through a pipe on the tinned surface, while it is just passing from the fused to the solid state; or a variety of delineations may be traced, by playing over the surface of the plate with the pointed flame of a blowpipe.

The following TABLE shows the several sizes of tin-plates, the marks by which they are distinguished, and their current wholesale prices in London:--

+------------------+---------+----+------+--------+----------------+
|Names. |Sizes. |No. |Weight|Marks |Prices per |
| | |in a|of |on the |box, in |
| | |box.|each |boxes. +--------+-------+
| | | |box. | | 1823. | 1838. |
+------------------+---------+----+------+--------+--------+-------+
| |_Inches._| |c q l| |_s._ |_s. d._|
|Common, No. 1. |13-3/4 by| | | | | |
| |10 | 225|1 0 0|CI. |47 | 35 |
| Ditto 2. |13-1/4 --| | | | | |
| | 9-1/4 | |0 3 21|CII. |45 | 33 6 |
| Ditto 3. |12-3/4 --| | | | | |
| | 9-1/2 | |0 3 16|CIII. |43 | 32 9 |
|Cross, No. 1. |13-3/4 --| | | | | |
| |10 | |1 1 0|XI. |53 | 40 2 |
|Two crosses, 1. | | |1 1 21|XXI. |58 | 43 2 |
|Three crosses, 1. | | |1 2 14|XXX. I. |63 | 47 |
|Four crosses, 1. | | |1 3 7|XXXX. I.| | |
|Common doubles |16-3/4 --| | | | | |
| |12-1/2 | 100|0 3 21|CD. |64-6} | 48 6 |
|Cross doubles | | |1 0 14|XD. |73-6}[A]| 56 |
|Two cross do. | | |1 1 7|XXD. |81 } | 60 6 |
|Three cross do. | | |1 2 0|XXXD. |88-6} | 65 |
|Four cross do. | | |1 2 21|XXXXD. | | |
|Com. small doubles| 5 -- 11| 200|1 2 0|CSD. |69 | 51 6 |
|Cross do. do. | | |1 2 21|XSD. |75 | 56 0 |
|Two cross do. | | |1 3 14|XXSD. |80 | 59 6 |
|Three do. do. | | |2 0 7|XXXSD. | | |
|Four do. do. | | |2 1 0|XXXXSD. | | |
|Waster’s com. | 3-3/4 --| | | | | |
|No. 1. |10 | 225|1 0 0|WCI. |44 | 32 9 |
|Ditto cross, 1.| ditto | |1 1 0|WXI. |50 | 47 3 |
+------------------+---------+----+------+--------+--------+-------+

c = _cwt._
q = _qrs._
l = _lbs._
[A] = 150 sheets in each.

These are the cash prices of one wholesale warehouse in Thames-street; an immediately adjoining warehouse charges fully 1_s._ more upon the standard CI, and proportionally upon the others.

TITANIUM, is a rare metal, discovered by Klaproth, in menachanite, in 1794. It has been detected since in the form of small cubes of a copper-red colour, in some of the blast furnaces in Yorkshire. According to Hassenfratz, its presence in small quantity does not impair the malleability of iron. It is very brittle, so hard as to scratch steel, and very light, having a specific gravity of only 5·3. It will not melt in the heat of any furnace, nor dissolve, when crystallized, even in nitro-muriatic acid; but only when in fine powder. By calcination with nitre, it becomes oxygenated, and forms titanate of potassa. Traces of this metal may be detected in many irons, both wrought and cast. The principal ores of titanium are _sphene_, common and foliated, _rutile_, _iserine_, _menachanite_, and _octahedrite_ or _pyramidal titanium ore_. None of them has been hitherto applied to any use.

TOBACCO. It is said that the name tobacco was given by the Spaniards to the plant, because it was first observed by them at Tabasco, or Tabaco, a province of Yucatan in Mexico. In 1560, Nicot, the French ambassador to Portugal, having received some tobacco from a Flemish merchant, showed it, on his arrival in Lisbon, to the grand prior, and, on his return into France, to Catherine of Medicis, whence it has been called Nicotiana by the botanists. Admiral Sir Francis Drake having, on his way home from the Spanish Main, in 1586, touched at Virginia, and brought away some forlorn colonists, is reported to have first imported tobacco into England. But, according to Lobel, this plant was cultivated in Britain before the year 1570; and was consumed by smoking in pipes by Sir Walter Raleigh, and companions, so early as the year 1584.

The plants are hung up to dry during four or five weeks; taken down out of the sheds in damp weather, for in dry they would be apt to crumble into pieces; stratified in heaps, covered up, and left to sweat for a week or two, according to their quality and the state of the season; during which time they must be examined frequently, opened up, and turned over, lest they become too hot, take fire, or run into putrefactive fermentation. This process needs to be conducted by skilful and attentive operatives. An experienced negro can form a sufficiently accurate judgment of the temperature, by thrusting his hand down into the heap.

The tobacco thus prepared, or often without fermentation, is sent into the market; but, before being sold, it must undergo the inspection of officers, appointed by the state with very liberal salaries, who determine its quality, and brand an appropriate stamp upon its casks, if it be sound; but if it be bad, it is burned.

Our respectable tobacconists are very careful to separate all the damaged leaves, before they proceed to their preparation, which they do by spreading them in a heap upon a stone pavement, watering each layer in succession, with a solution of sea salt, of spec. grav. 1·107, called _sauce_, till a ton or more be laid; and leaving their principles to react on each other for three or four days, according to the temperature, and the nature of the tobacco. It is highly probable that ammonia is the volatilizing agent of many odours, and especially of those of tobacco and musk. If a fresh green leaf of tobacco be crushed between the fingers, it emits merely the herbaceous smell common to many plants; but if it be triturated in a mortar, along with a little quicklime or caustic potash, it will immediately exhale the peculiar odour of snuff. Now analysis shows the presence of muriate of ammonia in this plant, and fermentation serves further to generate free ammonia in it; whence, by means of this process, and lime, the odoriferous vehicle is abundantly developed. If, on the other hand, the excess of alkaline matter in the tobacco of the shops be saturated by a mild dry acid, as the tartaric, its peculiar aroma will entirely disappear.

Tobacco contains a great quantity of an azotized principle, which by fermentation produces abundance of ammonia; the first portions of which saturate the acid juices of the plant, and the rest serve to volatilize its odorous principles. The salt water is useful chiefly in moderating the fermentation, and preventing it from passing into the putrefactive stage; just as salt is sometimes added to saccharine worts in tropical countries, to temper the fermentative action. The sea salt, or concentrated sea water, which contains some muriate of lime, tends to keep the tobacco moist, and is therefore preferable to pure chloride of sodium for this purpose. Some tobacconists mix molasses with the salt _sauce_, and ascribe to this addition the violet colour of the _macouba_ snuff of Martinique; and others add a solution of extract of liquorice. The following prescription is that used by a skilful manufacturer:--In a solution of the liquorice juice, a few figs are to be boiled for a couple of hours; to the decoction, while hot, a few bruised anise-seeds are to be added, and when cold, common salt to saturation. A little silent spirit of wine being poured in, the mixture is to be equably, but sparingly, sprinkled with the rose of a watering-pot, over the leaves of the tobacco, as they are successively stratified upon the preparation floor.

The fermented leaves, being next stripped of their middle ribs by the hands of children, are sorted anew, and the large ones are set apart for making cigars. Most of the tobaccos on sale in our shops are mixtures of different growths: one kind of smoking tobacco, for example, consists of 70 parts of Maryland, and 30 of meagre Virginia; and one kind of snuff consists of 80 parts of Virginia, and 30 parts of either Humesfort or Warwick. The Maryland is a very light tobacco, in thin yellow leaves; that of Virginia is in large brown leaves, unctuous or somewhat gluey on the surface, having a smell somewhat like the figs of Malaga; that of Havannah is in brownish, light leaves, of an agreeable and rather spicy smell; it forms the best cigars. The Carolina tobacco is less unctuous than the Virginian; but in the United States it ranks next to the Maryland.

The shag tobacco is dried to the proper point upon sheets of copper.

Tobacco is cut into what is called shag tobacco by knife-edged chopping stamps, a machine somewhat similar to that represented under METALLURGY, _fig._ 670. For grinding the tobacco leaves into snuff, conical mortars are employed, somewhat like that used by the Hindoos for grinding sugar-canes, _fig._ 1080.; but the sides of the snuff-mill have sharp ridges from the top to near the bottom.

Mr. L. W. Wright obtained a patent in August, 1827, for a tobacco-cutting machine, which bears a close resemblance to the well-known machines with revolving knives, for cutting straw into chaff. The tobacco, after being squeezed into cakes, is placed upon a smooth bed within a horizontal trough, and pressed by a follower and screws to keep it compact. These cakes are progressively advanced upon the bed, or fed in, to meet the revolving blades. The speed of the feeding-screw determines the degree of fineness of the sections or particles into which the tobacco is cut.

I was employed some years ago by the Excise, to analyze a quantity of snuff, seized on suspicion of having been adulterated by the manufacturer. I found it to be largely drugged with pearl-ashes, and to be thereby rendered very pungent, and absorbent of moisture; an economical method of rendering an effete article at the same time active and aqueous.

According to the recent analysis of Possett and Reimann, 10,000 parts of tobacco-leaves contain--6 of the peculiar chemical principle _nicotine_; 1 of _nicotianine_; 287 of slightly bitter extractive; 174 of gum, mixed with a little malic acid; 26·7 of a green resin; 26 of vegetable albumen; 104·8 of a substance analogous to gluten; 51 of malic acid; 12 of malate of ammonia; 4·8 of sulphate of potassa; 6·3 of chloride of potassium; 9·5 of potassa, which had been combined with malic and nitric acids; 16·6 of phosphate of lime; 24·2 of lime, which had been combined with malic acid; 8·8 of silica; 496·9 of fibrous or ligneous matter; traces of starch; and 88·28 of water.

_Nicotine_ is a transparent colourless liquid, of an alkaline nature. It may be distilled in a retort plunged into a bath heated to 290° Fahrenheit. It has a pricking, burning taste, which is very durable; and a pungent disagreeable smell. It burns by means of a wick, with the diffusion of a vivid light, and much smoke. It may be mixed with water in all proportions. It is soluble also in acetic acid, oil of almonds, alcohol, and ether, but not in oil of turpentine. It acts upon the animal economy with extreme violence; and in the dose of one drop it kills a dog. It forms salts with the acids. About one part of it may be obtained by very skilful treatment from one thousand of good tobacco.

Tobacco imported into the United Kingdom, viz.--unmanufactured, in 1836, 52,232,907 lbs.; in 1837, 27,070,448 lbs.;--manufactured, and snuff, in 1836, 182,248 lbs.; in 1837, 642,287 lbs. Retained for home consumption, unmanufactured, in 1836, 22,309,021 lbs.; in 1837, 22,504,343 lbs.:--manufactured, and snuff, in 1836, 159,226 lbs.; in 1837, 145,045 lbs. Duty received,--on unmanufactured tobacco, in 1836, _£_3,344,703; in 1837, _£_3,375,125; on manufactured tobacco, and snuff, in 1836, £71,560; in 1837, _£_65,220.

TOBACCO-PIPES. The practice of smoking tobacco has become so general in many nations as to render the manufacture of tobacco-pipes a considerable branch of industry. Some seek in the inhalation of tobacco-smoke a pleasurable narcotism; others imagine it to be beneficial to their health; but, in general, smoking is merely a dreamy resource against ennui, which ere long becomes an indispensable stimulus. The filthiness of this habit, the offensive odour which persons under its influence emit from their mouths and clothes, the stupor it too often occasions, as well as the sallow complexion, black or carious teeth, and impaired digestion, all prove the great consumption of tobacco to be akin in evil influence upon mankind to the use of ardent spirits.

Tobacco-pipes are made of a fine-grained plastic white clay, to which they have given the name. It is worked with water into a thin paste, which is allowed to settle in pits, or it may be passed through a sieve, to separate the siliceous or other stony impurities; the water is afterwards evaporated till the clay becomes of a doughy consistence, when it must be well kneaded to make it uniform. Pipe-clay is found chiefly in the isle of Purbeck and Dorsetshire. It is distinguished by its perfectly white colour, and its great adhesion to the tongue after it is baked; owing to the large proportion of alumina which it contains.

A child fashions a ball of clay from the heap, rolls it out into a slender cylinder upon a plank, with the palms of his hands, in order to form the stem of the pipe. He sticks a small lump to the end of the cylinder for forming the bowl; which having done, he lays the pieces aside for a day or two, to get more consistence. In proportion as he makes these rough figures, he arranges them by dozens on a board, and hands them to the pipemaker.

The pipe is finished by means of a folding brass or iron mould, channelled inside of the shape of the stem and the bowl, and capable of being opened at the two ends. It is formed of two pieces, each hollowed out like a half-pipe, cut as it were lengthwise; and these two jaws, when brought together, constitute the exact space for making one pipe. There are small pins in one side of the mould, corresponding to holes in the other, which serve as guides for applying the two together with precision.

The workman takes a long iron wire, with its end oiled, and pushes it through the soft clay in the direction of the stem, to form the bore, and he directs the wire by feeling with his left hand the progress of its point. He lays the pipe in the groove of one of the jaws of the mould, with the wire sticking in it; applies the other jaw, brings them smartly together, and unites them by a clamp or vice, which produces the external form. A lever is now brought down, which presses an oiled stopper into the bowl of the pipe, while it is in the mould, forcing it sufficiently down to form the cavity; the wire being meanwhile thrust backwards and forwards so as to pierce the tube completely through. The wire must become visible at the bottom of the bowl, otherwise the pipe will be imperfect. The wire is now withdrawn, the jaws of the mould opened, the pipe taken out, and the redundant clay removed with a knife. After drying for a day or two, the pipes are scraped, polished with a piece of hard wood, and the stems being bent into the desired form, they are carried to the baking kiln, which is capable of firing fifty gross in from 8 to 12 hours. A workman and a child can easily make five gross of pipes in a day.

No tobacco-pipes are so highly prized as those made in Natolia, in Turkey, out of meerschaum, a somewhat plastic magnesian stone, of a soft greasy feel, which is formed into pipes after having been softened with water. It becomes white and hard in the kiln.

A tobacco-pipe kiln should diffuse an equal heat to every part of its interior, while it excludes the smoke of the fire. The crucible, or large sagger, A, A, _figs._ 1155. and 1156., is a cylinder, covered in with a dome. It is placed over the fireplace B, and enclosed within a furnace of ordinary brickwork D, D, lined with fire-bricks E, E. Between this lining and the cylinder, a space of about 4 inches all round is left for the circulation of the flame. There are 12 supports or ribs between the cylinder and the furnace lining, which form so many flues, indicated by the dotted lines _x_, in _fig._ 1156. (the dotted circle representing the cylinder). These ribs are perforated with occasional apertures, as shown in _fig._ 1155., for the purpose of connecting the adjoining flues; but the main bearing of the hollow cylinder is given by five piers, _b_, _b_, _c_, formed of bricks projecting over and beyond each other. One of these piers _c_, is placed at the back of the fireplace, and the other four at the sides _b_, _b_. These project nearly into the centre, in order to support and strengthen the bottom; while the flues pass up between them, unite at the top of the cylinder in the dome L, and discharge the smoke by the chimney N.

The lining F, E, E, of the chimney is open on one side to form the door, by which the cylinder is charged and discharged. The opening is permanently closed as high as _k_, _fig._ 1155., by an iron plate plastered over with fire-clay; above this it is left open, and shut merely with temporary brickwork while the furnace is going. When this is removed, the furnace can be filled or emptied through the opening, the cylindric crucible having a correspondent aperture in its side, which is closed in the following ingenious way, while the furnace is in action. The workman first spreads a layer of clay round the edge of the opening, he then sticks the stems of broken pipes across from one side to the other, and plasters up the interstices with clay, exactly like the lath-and-plaster work of a ceiling. The whole of the cylinder, indeed, is constructed in this manner, the bottom being composed of a great many fragments of pipe stems, radiating to the centre; these are coated at the circumference with a layer of clay. A number of bowls of broken pipes are inserted in the clay; in these other fragments are placed upright to form the sides of the cylinder. The ribs round the outside, which form the flues, are made in the same way, as well as the dome L; by which means the cylindric case may be made very strong, and yet so thin as to require little clay in the building, a moderate fire to heat it, while it is not apt to split asunder. The pipes are arranged within, as shown in the figure, with their bowls resting against the circumference and their ends supported on circular pieces of clay _r_, which are set up in the centre for that purpose. Six small ribs are made to project inwards all round the crucible, at the proper heights, to support the different ranges of pipes, without having so many resting on each other as to endanger their being crushed by the weight. By this mode of distribution, the furnace may contain 50 gross, or 7200 pipes, all baked within 8 or 9 hours; the fire being gradually raised, or damped if occasion be, by a plate partially slid over the chimney top.

TODDY, _Sura_, _Mee-ra_, sweet juice.--The proprietors of coco-nut plantations in the peninsula of India, and in the Island of Ceylon, instead of collecting a crop of nuts, frequently reap the produce of the trees by extracting sweet juice from the flower-stalk. When the flowering branch is half shot, the toddy-drawers bind the stock round with a young coco-nut leaf in several places, and beat the spadix with a short baton of ebony. This beating is repeated daily for ten or twelve days, and about the end of that period a portion of the flower-stalk is cut off. The stump then begins to bleed, and an earthen vessel (chatty) or a calabash is suspended under it, to receive the juice, which is by the Europeans called _toddy_.

A thin slice is taken from the stump daily, and the toddy is removed twice a day. A coco-nut frequently pushes out a new _spadix_ once a month; and after each spadix begins to bleed, it continues to produce freely for a month, by which time another is ready to supply its place. The old spadix continues to give a little juice for another month, after which it withers; so that there are sometimes two pots attached to a tree at one time, but never more. Each of these spadices, if allowed to grow, would produce a bunch of nuts from two to twenty. Trees in a good soil produce twelve bunches in the year; but when less favourably situated, they often do not give more than six bunches. The quantity of six English pints of toddy is sometimes yielded by a tree daily.

Toddy is much in demand as a beverage in the neighbourhood of villages, especially where European troops are stationed. When it is drunk before sunrise, it is a cool, delicious, and particularly wholesome beverage; but by eight or nine o’clock fermentation has made some progress, and it is then highly intoxicating.[68]

[68] Contributions to the History of the Coco-nut Tree. By Henry
Marshall, Esq., Deputy Inspector of Hospitals.

TOLU, is a brownish-red balsam, extracted from the stem of the _Myroxilon toluiferum_, a tree which grows in South America. It is composed of resin, oil, and benzoic acid. Having an agreeable odour, it is sometimes used in perfumery. It has a place in the Materia Medica, but for what good reason I know not.

TOMBAC, is a white alloy of copper.

TONKA BEAN, the fruit of the _Dipterix odorata_, affords a concrete crystalline volatile oil (_stearoptène_), called _coumarine_ by the French. It is extracted by digestion with alcohol, which dissolves the stearoptène, and leaves a fat oil. It has an agreeable smell, and a warm taste. It is fusible at 122° Fahrenheit, and volatile at higher heats.

TOPAZ. See LAPIDARY.

TORTOISE-SHELL, or rather scales, a horny substance, that covers the hard strong covering of a bony contexture, which encloses the _Testudo imbricata_, Linn. The lamellæ or plates of this tortoise are 13 in number, and may be readily separated from the bony part by placing fire beneath the shell, whereby they start asunder. They vary in thickness from one-eighth to one-quarter of an inch, according to the age and size of the animal, and weigh from 5 to 25 pounds. The larger the animal, the better is the shell. This substance may be softened by the heat of boiling water; and if compressed in this state by screws in iron or brass moulds, it may be bent into any shape. The moulds being then plunged in cold water, the shell becomes fixed in the form imparted by the mould. If the turnings or filings of tortoise-shell be subjected skilfully to gradually increased compression between moulds immersed in boiling water, compact objects of any desired ornamental figure or device may be produced. The soldering of two pieces of scale is easily effected, by placing their edges together, after they are nicely filed to one bevel, and then squeezing them strongly between the long flat jaws of hot iron pincers, made somewhat like a hairdresser’s curling-tongs. The pincers should be strong, thick, and just hot enough to brown paper slightly, without burning it. They may be soldered also by the heat of boiling water, applied along with skilful pressure. But in whatever way this process is attempted, the surfaces to be united should be made very smooth, level, and clean; the least foulness, even the touch of a finger, or breathing upon them, would prevent their coalescence. See HORN.

TOUCH-NEEDLES, and TOUCH-STONE, are means of ascertaining the quality of gold trinkets. See ASSAY.

TOW. See FLAX.

TRAGACANTH, GUM. (_Gomme adracante_, Fr.; _Traganth_, Germ.) See GUM.

TRAVERTINO. See TUFA.

TREACLE, is the viscid brown uncrystallizable syrup which drains from the sugar-refining moulds. Its specific gravity is generally 1·4, and it contains upon an average 75 per cent. of solid matter, by my experiments.

TRIPOLI (_Terre pourrie_, Fr.; _Tripel_, Germ.); rotten-stone; is a mineral of an earthy fracture, a yellowish-gray or white colour, composition impalpably fine, meagre to the touch, does not adhere to the tongue, and burns white. Its analogue, the _Polierschiefer_, occurs in thin flat foliated pieces, of the above colours, occasionally striped; soft, absorbent of water; spec. grav. 1·9. to 2·2.

M. Ehrenberg has shown that both of these friable homogeneous rocks, which consist almost entirely of silica, are actually composed of the exuviæ or rather the skeletons of infusoria (_animalcula_) of the family of _Barcillariæ_, and the genera _Cocconema_, _Gonphonema_, &c. They are recognised with such distinctness in the microscope, that their analogies with living species may be readily traced; and in many cases there are no appreciable differences between the living and the petrified. The species are distinguished by the number of partitions or transverse lines upon their bodies. The length is about 1/288 of a line. M. Ehrenberg made his observations upon the tripolis of Billen in Bohemia of Santafiora in Tuscany, of the Isle of France, and of Francisbad, near Eger.

The meadow iron ore (_Fer limoneux des marais_) is composed almost wholly of the _Gaellonella ferruginea_. Most of these infusoria are lacustrine; but others are marine, particularly the _tripolis_ of the Isle of France.

According to the chemical analysis of Bucholz, tripoli consists of--silica, 81; alumina, 1·5; oxide of iron, 8; sulphuric acid, 3·45; water, 4·55. This specimen was probably found in a coal-field. The tripoli of Corfu is reckoned the best for scouring or brightening brass and other metals. Mr. Phillips found in the Derbyshire rotten-stone (near Bakewell), 86 of alumina, 4 of silica, and 10 of carbon--being a remarkable difference in composition from the Bohemian.

TUFA, or TUF, is a gray deposit of calcareous carbonate, from springs and streams.

TULA METAL, is an alloy of silver, copper, and lead.

TUNGSTEN (Eng. and Fr.; _Wolfram_, Germ.); is a peculiar metal, which occurs in the state of an acid (the _tungstic_), combined with various bases, as with lime, the oxides of iron, manganese, and lead. The metal is obtained by reduction of the ore, or the deoxidizement of the acid, in the form of a dark steel-gray powder, which assumes under the burnisher a feeble metallic lustre. Its specific gravity is 17·22.

TURBITH MINERAL, is the yellow subsulphate of mercury.

TURF (_Peat_, Scotch; _Tourbe_, Fr.; _Torf_, Germ.); consists of vegetable matter, chiefly of the moss family, in a state of partial decomposition by the action of water. Cut, during summer, into brick-shaped pieces, and dried, it is extensively used as fuel by the peasantry in every region where it abounds. The dense black turf, which forms the lower stratum of a peat-moss, is much contaminated with iron, sulphur, sand, &c., while the lighter turf of the upper strata, though nearly pure vegetable matter, is too bulky for transportation, and too porous for factory fuel. These defects have been happily removed by Mr. Williams, managing director of the Dublin Steam Navigation Company, who has recently obtained a patent for a method of converting the lightest and purest beds of peat-moss, or bog, into the four following products: 1. A brown combustible solid, denser than oak; 2. A charcoal, twice as compact as that of hard wood; 3. A factitious coal; and 4. A factitious coke; each of which possesses very valuable properties.

Mr. D’Ernst, artificer of fire-works to Vauxhall, has proved, by the severe test of coloured fires, that the turf charcoal of Mr. Williams is 20 per cent. more combustible than that of oak. Mr. Oldham, engineer of the Bank of England, has applied it in softening his steel plates and dies, with remarkable success. But one of the most important results of Mr. Williams’s invention is, that with 10 cwts. of pitcoal, and 2-1/2 cwts. of his factitious coal, the same steam power is now obtained, in navigating the Company’s ships, as with 17-1/2 cwts. of pitcoal alone; thereby saving 30 per cent. in the stowage of fuel. What a prospect is thus opened up of turning to admirable account the unprofitable bogs of Ireland; and of producing, from their inexhaustible stores, a superior fuel for every purpose of arts and engineering.

The turf is treated as follows:--Immediately after being dug, it is triturated under revolving edge-wheels, faced with iron plates perforated all over their surface, and is forced by the pressure through these apertures, till it becomes a species of pap, which is freed from the greater part of its moisture by squeezing in a hydraulic press between layers of caya cloth, then dried, and coked in suitable ovens.--(See CHARCOAL, and PITCOAL, COKING OF.) Mr. Williams makes his factitious coal by incorporating with pitch or rosin, melted in a cauldron, as much of the above charcoal, ground to powder, as will form a doughy mass, which is moulded into bricks in its hot and plastic state. From the experiments of M. Le Sage, detailed in the 5th volume of “The Repertory of Arts,” charred ordinary turf seems to be capable of producing a far more intense heat than common charcoal. It has been found preferable to all other fuel for case-hardening iron, tempering steel, forging horseshoes, and welding gun-barrels. Since turf is partially carbonized in its native state, when it is condensed by the hydraulic press, and fully charred, it must evidently afford a charcoal very superior in calorific power to the porous substance generated from wood by fire.

TURKEY RED, is a brilliant dye produced on cotton goods by MADDER.

TURMERIC, _Curcuma_, _Terra merita_, (_Souchet_, or _Safran des Indes_, Fr.; _Gelbwurzel_, Germ.); is the root of the _Curcuma longa_ and _rotunda_, a plant which grows in the East Indies, where it is much employed in dyeing yellow, as also as a condiment in curry sauce or powder. The root is knotty, tubercular, oblong, and wrinkled; pale-yellow without, and brown-yellow within; of a peculiar smell, a taste bitterish and somewhat spicy. It contains a peculiar yellow principle, called _curcumine_, a brown, colouring-matter, a volatile oil, starch, &c. The yellow tint of turmeric is changed to brown-red by alkalis, alkaline earths, subacetate of lead, and several metallic oxides; for which reason, paper stained with it is employed as a chemical test.

Turmeric is employed by the wool-dyers for compound colours which require an admixture of yellow, as for cheap browns and olives. As a yellow dye, it is employed only upon silk. It is a very fugitive colour. A yellow lake may be made by boiling turmeric powder with a solution of alum, and pouring the filtered decoction upon pounded chalk.

TURNSOLE. See ARCHIL and LITMUS.

TURQUOIS. See LAPIDARY.

TURPENTINE (_Térébinthine_, Fr.; _Terpenthin_, Germ.); is a substance which flows out of incisions made in the stems of several species of pines. It has the consistence and gray-yellow colour of honey. It has a smell which is not disagreeable to many persons, a warm, sharp, bitterish taste; dries into a solid in the air, with the evaporation of its volatile oil. It becomes quite fluid at a moderate elevation of temperature, and burns at a higher heat, with a bright but very fuliginous flame. There are several varieties of turpentine.

1. _Common turpentine_, is extracted from incisions in the _Pinus abies_ and _Pinus silvestris_. It has little smell; but a bitter burning taste. It consists of the volatile oil of turpentine to the amount of from 5 to 25 per cent.; and of rosin or colophony.

2. _Venice turpentine_, is extracted from the _Pinus larix_ (larch), and the French turpentine from the _Pinus maritima_. The first comes from Styria, Hungary, the Tyrol, and Switzerland, and contains from 18 to 25 per cent. of oil; the second, from the south of France, and contains no more than 12 per cent. of oil. The oil of all the turpentines is extracted by distilling them along with water. They dissolve in all proportions in alcohol, without leaving any residuum. They also combine with alkaline lyes, and in general with the salifiable bases. Venice turpentine contains also succinic acid.

3. Turpentine of Strasbourg is extracted from the _Pinus picea_ and _Abies excelsa_. It affords 33·5 per cent. of volatile oil, and some volatile or crystallizable resin, with extractive matter and succinic acid.

4. Turpentine of the Carpathian mountains, and of Hungary; the first of which comes from the _Pinus cembra_, and the second from the _Pinus mugos_. They resemble that of Strasbourg.

5. Turpentine of Canada, called Canada balsam, is extracted from the _Pinus canadensis_ and _balsamea_. Its smell is much more agreeable than that of the preceding species.

6. Turpentine of Cyprus or Chio, is extracted from the _Pistacea terebinthus_. It has a yellow, greenish, or blue-green colour. Its smell is more agreeable, and taste less acrid, than those of the preceding sorts.

Common Turpentine imported into the United Kingdom, in 1836, 370,981 cwts. 1 qr. 26 lbs.; in 1837, 415,023 cwts. 1 qr. 10 lbs. Retained for home consumption, in 1836, 341,693 cwts. 18 lbs.; in 1837, 405,772 cwts. 2 qrs. 14 lbs. Duty received, in 1836, _£_74,052; in 1837, _£_87,918.

TURPENTINE, OIL OF, sometimes called essence of turpentine. As found in commerce, it contains more or less rosin, from which it may be freed by re-distillation along with water. It is colourless, limpid, very fluid, and possessed of a very peculiar smell. Its specific gravity, when pure, is 0·870; that of the oil commonly sold in London, is 0·875. It always reddens litmus paper, from containing a little succinic acid. According to Oppermann, the oil which has been repeatedly rectified over chloride of calcium, consists of 84·60 carbon, 11·735 hydrogen, and 3·67 oxygen. When oil of turpentine contains a little alcohol, it burns with a clear flame; but otherwise it affords a very smoky flame. Chlorine inflames this oil; and muriatic acid converts it into a crystalline substance, like camphor. It is employed extensively in varnishes, paints, &c., as also in medicine.

TUTENAG, is an alloy of copper and zinc.

TYPE, (_Caractère_, Fr.; _Druckbuchstabe_, Germ.) The first care of the letter-cutter is to prepare well-tempered steel punches, upon which he draws or marks the exact shape of the letter, with pen and ink if it be large, but with a smooth blunted point of a needle if it be small; and then, with a proper sized and shaped graver and sculpter, he digs or scoops out the metal between the strokes upon the face of the punch, leaving the marks untouched and prominent. He next works the outside with files till it be fit for the matrix. Punches are also made by hammering down the hollows, filing up the edges, and then hardening the soft steel. Before he proceeds to sink and justify the matrix, he provides a mould to justify them by, of which a good figure is shown in plate XV., _Miscellany_, _figs._ 2. 3. of _Rees’s Cyclopædia_.

A matrix is a piece of brass or copper, about an inch and a half long, and thick in proportion to the size of the letter which it is to contain. In this metal the face of the letter intended to be cast is sunk, by striking it with the punch to a depth of about one eighth of an inch. The mould, _fig._ 1157., in which the types are cast, is composed of two parts. The outer part is made of wood, the inner of steel. At the top it has a hopper-mouth _a_, into which the fused type-metal is poured. The interior cavity is as uniform as if it had been hollowed out of a single piece of steel; because each half, which forms two of the four sides of the letter, is exactly fitted to the other. The matrix is placed at the bottom of the mould, directly under the centre of the orifice, and is held in its position by a spring _b_. Every letter that is cast can be loosened from the matrix only by removing the pressure on the spring.

A good type-foundry is always provided with several furnaces, each surmounted with an iron pot containing the melted alloy, of 3 parts of lead and 1 of antimony. Into this pot the founder dips the very small iron ladle, to lift merely as much metal as will cast a single letter at a time. Having poured in the metal with his right hand, and returned the ladle to the melting-pot, the founder throws up his left hand, which holds the mould, above his head, with a sudden jerk, supporting it with his right hand. It is this movement which forces the metal into all the interstices of the matrix; for without it, the metal, especially in the smaller moulds, would not be able to expel the air and reach the bottom. The pouring in the metal, the throwing up the mould, the unclosing it, removing the pressure of the spring, picking out the cast letter, closing the mould again, and re-applying the spring to be ready for a new operation, are all performed with such astonishing rapidity and precision, that a skilful workman will turn out 500 good letters in an hour, being at the rate of one every eighth part of a minute. A considerable piece of metal remains attached to the end of the type as it quits the mould. There are nicks upon the lower edge of the types, to enable the compositor to place them upright, without looking at them.

From the table of the _caster_, the heap of types turned out of his mould, is transferred from time to time to another table, by a boy, whose business it is to break off the superfluous metal, and that he does so rapidly as to clear from 2000 to 5000 types in an hour; a very remarkable dispatch, since he must seize them by their edges, and not by their feeble flat sides. From the breaking-off boy, the types are taken to the _rubber_, a man who sits in the centre of the workshop with a grit-stone slab on a table before him, and having on the fore and middle finger of his right hand a piece of tarred leather, passes each broad side of the type smartly over the stone, turning it in the movement, and that so dexterously, as to be able to rub 2000 types in an hour.

From the rubber, the types are conveyed to a boy, who, with equal rapidity sets them up in lines, in a long shallow frame, with their faces uppermost and nicks outwards. This frame, containing a full line, is put into the dresser’s hands, who polishes them on each side, and turning them with their faces downwards, cuts a groove or channel in their bottom, to make them stand steadily on end. It is essential that each letter be perfectly symmetrical and square; the least inequality of their length would prevent them from making a fair impression; and were there the least obliquity in their sides, it would be quite impossible, when 200,000 single letters are combined, as in one side of the _Times_ newspaper, that they could hold together as they require to do, when wedged up in the chases, as securely as if that side of type form a solid plate of metal. Each letter is finally tied up in lines of convenient length, the proportionate numbers of each variety, small letters, points, large capitals, small capitals, and figures, being selected, when the fount of type is ready for delivery to the printer.

The sizes of types cast in this country vary, from the smallest, called diamond, of which 205 lines are contained in a foot length, to those letters employed in placards, of which a single letter may be 3 or 4 inches high. The names of the different letters and their dimensions, or the number of lines which each occupies in a foot, are stated in the following table:--

Double Pica 41-1/2
Paragon 44-1/2
Great Primer 51-1/4
English 64
Pica 71-1/2
Small Pica 83
Long Primer 89
Bourgeois 102-1/4
Brevier 112-1/2
Minion 128
Nonpareil 143
Pearl 178
Diamond 205

T. Aspinwall, Esq., the American consul, obtained, in May, 1828, a patent for an improved method of casting printing types by means of a mechanical process, being a communication from a foreigner residing abroad. The machine is described, with six explanatory figures, in the second series of Newton’s Journal, vol. v. page 212. The patentee does not claim, as his invention, any of the parts separately, but the general process and arrangement of machinery; more particularly the manner of suspending a swing table (upon which the working parts are mounted) out of the horizontal and perpendicular position; the mode of moving the table with the parts of the mould towards the melting-pot; the manner of bringing the parts of the mould together, and keeping them closed during the operation of casting the types. Several other mechanical schemes have been proposed for founding types, but I have been informed by very competent judges, Messrs. Clowes, that none of them can compete in practical utility with that dexterity and precision of handiwork, which I have often seen practised in their great printing establishment in Stamford-street.

U.

ULTRAMARINE (_Outremer_, Fr.; _Ultramarins_, Germ.); is a beautiful blue pigment obtained from the variegated blue mineral, called lazulite (_lapis lazuli_), by the following process:--Grind the stone to fragments, rejecting all the colourless bits, calcine at a red heat, quench in water, and then grind to an impalpable powder along with water, in a paint-mill, (see PAINTS, GRINDING OF,) or with a porphyry slab and muller. The paste being dried, is to be rubbed to powder, and passed through a silk sieve. 100 parts of it are to be mixed with 40 of rosin, 20 of white wax, 25 of linseed oil, and 15 of Burgundy pitch, previously melted together. This resinous compound is to be poured hot into cold water; kneaded well first with two spatulas, then with the hands, and then formed into one or more small rolls. Some persons prescribe leaving these pieces in the water during 15 days, and then kneading them in it, whereby they give out the blue pigment, apparently because the ultramarine matter adheres less strongly than the _gangue_, or merely siliceous matter of the mineral, to the resinous paste. MM. Clement and Desormes, who were the first to divine the true nature of this pigment, think that the soda contained in the lazulite, uniting with the oil and the rosin, forms a species of soap, which serves to wash out the colouring-matter. If it should not separate readily, water heated to about 150° F. should be had recourse to. When the water is sufficiently charged with blue colour, it is poured off and replaced by fresh water; and the kneading and change of water are repeated till the whole of the colour is extracted. Others knead the mixed resinous mass under a slender stream of water, which runs off with the colour into a large earthen pan. The first waters afford, by rest, a deposit of the finest ultramarine; the second, a somewhat inferior article, and so on. Each must be washed afterwards with several more waters, before they acquire the highest quality of tone; then dried separately, and freed from any adhering particles of the pitchy compound by digestion in alcohol. The remainder of the mass being melted with oil, and kneaded in water containing a little soda or potash, yields an inferior pigment, called _ultramarine ashes_. The best _ultramarine_ is a splendid blue pigment, which works well with oil, and is not liable to change by time. Its price in Italy was five guineas the ounce, a few years ago, but it is now greatly reduced.

The blue colour of _lazulite_ had been always ascribed to iron, till MM. Clement and Desormes, by a most careful analysis, showed it to consist of--silica, 34; alumina, 33; sulphur, 3; soda, 22; and that the iron, carbonate of lime, &c. were accidental ingredients, essential neither to the mineral, nor to the pigment made from it. By another analyst, the constituents are said to be--silica, 44; alumina, 35; and soda, 21; and by a third, potassa was found instead of soda, showing shades of difference in the composition of the stone.

Till a few years ago, every attempt failed to make ultramarine artificially. At length, in 1828, M. Guimet resolved the problem, guided by the analysis of MM. Clement and Desormes, and by an observation of M. Tassaert, that a blue substance like ultramarine was occasionally produced on the sandstone hearths of his reverberatory soda furnaces. Of M. Guimet’s finest pigment I received a bottle several years ago, from my friend M. Merimée, secretary of the _Ecole de Beaux Arts_, which has been found by artists little, if any, inferior to the lazulite ultramarine. M. Guimet sells it at 60 francs per pound French,--which is little more than two guineas the English pound. He has kept his process secret. But M. Gmelin, of Tübingen, has published a prescription for making it; which consists in enclosing carefully in a Hessian crucible a mixture of 2 parts of sulphur, and 1 of dry carbonate of soda, heating them gradually to redness till the mass fuses, and then sprinkling into it by degrees another mixture, of silicate of soda, and aluminate of soda; the first containing 72 parts of silica, and the second 70 parts of alumina. The crucible must be exposed after this for an hour to the fire. The ultramarine will be formed by this time; only it contains a little sulphur, which can be separated by means of water. M. Persoz, professor of chemistry at Strasbourg, has likewise succeeded in making an ultramarine, of perhaps still better quality than that of M. Guimet. Lastly, M. Robiquet has announced, that it is easy to form ultramarine, by heating to redness a proper mixture of kaolin (China clay), sulphur, and carbonate of soda. It would therefore appear, from the preceding details, that ultramarine may be regarded as a compound of silicate of alumina, silicate of soda, with sulphuret of sodium; and that to the reaction of the last constituent upon the former two, it owes its colour.

UMBER, is a massive mineral; fracture large and flat; conchoidal in the great, very fine earthy in the small; dull; colour, liver, chestnut,--dark yellowish brown; opaque; does not soil, but writes; adheres strongly to the tongue, feels a little rough and meagre, and is very soft; specific gravity 2·2. It occurs in beds with brown jasper in the Island of Cyprus, and is used by painters as a brown colour, and to make varnish dry quickly.

URANIUM, is a rare metal, first discovered by Klaproth, in the black mineral called _pechblende_, found in a mine near Johann-Georgen-Stadt, in Saxony, and which is a sulphuret of uranium. A double phosphate of uranium and copper, called _green uranite_, and _uran mica_, occurs in Cornwall. It has been reduced to the metallic state by various devices, but it has hardly the appearance of metal to the naked eye, and from the rarity of its ores is not likely to be of any importance in the arts.

URAO, is the native name of a sesquicarbonate of soda found at the bottom of certain lakes in Mexico, especially to the north of Zacatecas, and in several other provinces; also in South America at Columbia, 48 English miles from Merida.

V.

VALONIA, is a kind of acorn, imported from the Levant and the Morea for the use of tanners, as the husk or cup contains abundance of tannin. The quantity imported for home consumption in 1836, was 80,511 cwts.; of which Turkey furnished 58,724, Italy and the Italian islands, 7209.

VANADIUM, is a metal discovered by Sefström, in 1830, in a Swedish iron, remarkable for its ductility, extracted from the iron mine of Jaberg, not far from Jönköping. Its name is derived from Vanadis, a Scandinavian idol. This metal has been found in the state of vanadic acid, in a lead ore from Zimapan, in Mexico. The finery cinders of the Jaberg iron contain more vanadium than the metal itself. It exists in it as vanadic acid. For the reduction of this acid to vanadium, see Berzelius’s _Traité de Chimie_, vol. iv. p. 644. Vanadium is white, and when its surface is polished, it resembles silver or molybdenum more than any other metal. It combines with oxygen into two oxides and an acid.